    塑料滑动摩擦磨损试验机

    塑料滑动摩擦磨损试验机 适用范围及功能符合标准:GB/T 3960-1983 塑料滑动摩擦磨...

    详细描述

    塑料滑动摩擦磨损试验机  适用范围及功能

    符合标准:GB/T 3960-1983 塑料滑动摩擦磨损试验方法 GB/T 9141.8-1999 柔性石墨板材滑动摩擦系数测试方法

    另外本厂生产的计算机控制塑料滑动摩擦试验机是在现有电子塑料滑动摩擦试验机的基础上又增加了很多试验功能,可以同时显示扭矩-时间曲线,随意设定试验次数,显示当前试验次数,

    设定时间及当前试验时间等多种功能,本机还配有彩色打印机,可以打印出带有曲线,表格数据,试验单位名头的精美的试验报告单。

    塑料滑动摩擦磨损试验机  试验步骤

    1、圆环应清除油污,贮存于干燥缸内以防生锈。

    2、试样经状态调节后用感量为0.1毫克的分析天平称取其质量(M1)。

    3、把试样装进夹具,摩擦面用角尺校正并使它与圆环的交线外于试样正中。装好摩擦力矩记录纸,开机校好零点。

    4、再次用乙醇、丙酮等不与塑料起作用的溶剂仔细清除试样和圆环上的油污,此后不准再用手接触试样和圆环的表面。

    5、平稳地加荷至选定的负荷值。

    6、对磨2小时后停机卸负荷,取下试样和圆环,清理试样表面后,用精度不低于0.02毫米的量具测量磨痕宽度,或在试验环境下存放1小时后称取试样质量(m2)

    7、读取摩擦力矩值。

    Characteristic:

    1. The system runs steadily and has high reliability.

    2. The structure is compact, easy to use and simple.

    3, using high precision motor, drive and sensor, high accuracy.

    4. It has the function of grading management of the testers.

    5, real-time display of friction coefficient time, torque time curve.

    6. The test report can print experimental parameters, test data, curves, remarks and other information. It is simple, convenient and editable.

    状态调节

    状态调节按GB2918-82《塑料试样状态调节和试验的标准环境》进行,温度为23±5摄氏度,温度为50±10%

    Functional characteristics:

    1, sample size: 30mm x 7mm x 6mm

    2, rotation speed: 0-500 turn / points (adjustable)

    3, load: 196N + 0.1% (can be increased to 392N)

    4, the size of the friction ring is: 40 x 10mm, chamfer 0.5 * 45 degrees, and the concentricity deviation between the outer surface and the inner circle is less than 0.01.

    5, friction ring material: 45 steel, quenching, heat treatment HRC40-45, round surface finish 8

    6, friction moment: 0--4N. M

    7, weight weight: 4KG weight one, 1KG weight 4, can achieve weight superposition function.

    试验条件

    试验中上转轴保持静止,下转轴以200/分转动,摩擦副做滑动摩擦,对磨2小时,负荷20公斤,根据材料,允许选择其它负荷.试验环境温度为23±5摄氏度.

    试验设备

    1、传动系统,用来带动圆环以给定的转速旋转,精确到5%以内,并要求圆环安装部位轴的径向跳动小于0.01毫米。

    2、加载系统,对试样和圆环,可施加法向力,精确到5%以内。

    3、测定和记录摩擦力矩系统,精确到5%以内。

    4、记录圆环转数的计数器或记时器,精确到1%以内。

    5、试样夹具结构和尺寸见图2,并附配垫圈 4 GB 848-76,沉头螺钉M3×0.3510毫米。要保证试样安置后无轴向窜动。

    注:试验设备本标准推荐采用M-200型磨损试验机。

    6、本试验中圆环的材质对塑料磨损试验结果影响很大,因此本标准采用的圆环,其外形尺寸见图3

    材料为45号钢,圆环要求整体淬火,热处理HRC 4045,外圆表面光洁度▽8,倒角处均为0.5×45度,外圆表面与内圆同心度偏差小于0.01.

        圆环可以反复使用,每次试验后,需重新磨削。当外径小于36毫米就不能再用。作仲裁试验时必须用直径40毫米的圆环。

    注:圆环材质也可按产品标准另定。

    试验报告

    试验报告应包括下列内容:

    A.塑料名称、规格、牌号、生产厂;

    B.试样的制备方法,摩擦表面状况,测定的试样个数;

    C.环境温度、温度及状态调节条件;

    D.圆环材质、硬度、光洁度和外径尺寸;

    E.试验负荷;

    F.试验结果:磨痕宽度或体积磨损及摩擦系数的测定结果;

    G.试验日期、人员。

    Functional characteristics:

    1, sample size: 30mm x 7mm x 6mm

    2, rotation speed: 0-500 turn / points (adjustable)

    3, load: 196N + 0.1% (can be increased to 392N)

    4, the size of the friction ring is: 40 x 10mm, chamfer 0.5 * 45 degrees, and the concentricity deviation between the outer surface and the inner circle is less than 0.01.

    5, friction ring material: 45 steel, quenching, heat treatment HRC40-45, round surface finish 8

    6, friction moment: 0--4N. M

    7, weight weight: 4KG weight one, 1KG weight 4, can achieve weight superposition function.

    test equipment

    1. The transmission system is used to drive the ring to rotate at a given speed, accurate to within 5%, and requires the radial runout of the shaft at the installation position of the ring to be less than 0.01 millimeters.

    2. The loading system can apply a normal force to the specimen and ring, accurate to within 5%.

    3. Measure and record the friction torque system with an accuracy of within 5%.

    4. A counter or timer that records the number of revolutions of a circle, accurate to within 1%.

    5. The structure and dimensions of the sample fixture are shown in Figure 2, accompanied by washers 4 GB 848-76 and countersunk screws M3 × 0.35 millimeters long. Ensure that there is no axial displacement of the sample after placement.

    Note: This standard recommends the use of M-200 wear testing machine for testing equipment.

    6. The material of the circular ring in this experiment has a significant impact on the plastic wear test results. Therefore, the outer dimensions of the circular ring used in this standard are shown in Figure 3.

    The material is 45 steel, and the ring requires overall quenching. The heat treatment is HRC 40-45, and the surface smoothness of the outer circle is 8. The chamfer is 0.5 × 45 degrees, the deviation between the concentricity of the outer surface and the inner surface is less than 0.01

    The ring can be reused and needs to be re ground after each test. When the outer diameter is less than 36 millimeters, it cannot be used again. When conducting arbitration tests, a circular ring with a diameter of 40 millimeters must be used.

    Note: The material of the circular ring can also be determined according to the product standard.

    功能特点:

    1、试样尺寸: 30mm×7mm×6mm

    2、转动速度: 0-500/分 (可调)

    3、负 荷: 196N ± 0.1%(可增至392N

    4、摩擦环尺寸:¢40×10mm ,倒角0.5×45°,外圆表面与内圆同心度偏差小于0.01

    5、摩擦环材质:45号钢,淬火,热处理HRC40-45,外圆表面光洁度▼8

    6、摩擦力矩: 0--4N·m

    7、砝码重量:4KG砝码一件,1KG砝码4件,可实现重量叠加功能。

    摩擦磨损定义

    1、摩擦:两物体接触表面间产生阻碍切向相对移动的现象称为摩擦。

    2、滑动摩擦:两接触物体接触点具有不同速度时之摩擦。

    3、摩擦力:两物体摩擦时相对移动的阻力。

    4、摩擦系数:阻碍两物体相对运动的摩擦力对作用到物体表面的法向力之比。

    5、磨损:物体相对运动时相互接触表面的物质不断损失或产生残余变形称为磨损。

    Test conditions

    During the experiment, the upper shaft remained stationary while the lower shaft rotated at 200 revolutions per minute. The friction pair was subjected to sliding friction for 2 hours, with a load of 20 kilograms. Depending on the material, other loads were allowed. The test environment temperature was 23 ± 5 degrees Celsius

    符合标准:

    GB/T 3960-1983 塑料滑动摩擦磨损试验方法 GB/T 9141.8-1999 柔性石墨板材滑动摩擦系数测试方法

    温度和速度的影响

    1.橡胶的摩擦性能具有明显的粘弹特征

    2.摩擦系数是温度和速度的函数,在某一速度和温度下出现极大值

    3.磨耗,一般来说,温度升高会使磨耗量增大,随着温度的降低,在玻璃化温度附近,磨耗量达到最小值,然后重新上升。

    表面状态的影响

    摩擦表面粗糙程度。润滑剂的存在,磨损碎片,橡胶表面老化和环境湿度都会大大改变橡胶的摩擦性能

    1.表面状态不同时,摩擦的粘附成分变化明显,特别是有润滑剂时,粘附摩擦成分显著减少。

    2.润滑和在橡胶制品表面涂有低摩擦系数的塑料,可以使摩擦系数减小,增大疲劳磨耗的成分,从而使磨耗减少。

    环境的影响

    周围的气体,液体,湿度对磨耗性能的影响是很大的

    1.氧气的存在对疲劳磨耗影响最大,但对粗糙表面上的磨耗影响不大

    2.液体介质使橡胶溶胀,从而降低耐磨性

    Function:

    The computer controlled plastic sliding friction test machine produced by our factory is on the basis of the existing electronic plastic sliding friction test machine, and has added a lot of test functions. It can display the torque time curve at the same time, set the test times at will, display the current test times, set the time and the current test time and other functions, this machine is this machine. It also has a color printer, which can print out exquisite test reports with curves, table data and test units.

    本机采用高精度扭矩传感器,16 位单片机电子处理系统,使得本仪器各项测试指标精度非常高。由于集成程度很高,所以设备本身的稳定性极好,本机具有一次设置,全自动运行,实验结束后自动停机,

    并检测磨损程度,同时通过打印机打印试验数据等功能。是各个科研单位,大学,企业实验室的必备检测设备。

    安全注意事项:开机之前,敬请仔细阅读本 使用指南,以防止出现对操作人员的意外伤害或对仪器的损坏等的事件。操作前,请阅读“安装与设置”,保证对仪器各部件的正确安装与连接。在第一次操作前,务必请有操作经验的人员进行指导,防止误操作造成意外事件的发生。电击危险: 确保在安装或维修该仪器之前使所有导线断电,防止在带电情况下,对人员或设备造成伤害。

    北广精仪公司电性能及橡胶塑料相关产品:

    BWN拉力材料试验机(符合国标GB/T1172-1999GB/T2975-1998GB/T10632-1989

    BDJC-10KV-200KV电压击穿试验仪(符合国标GB1408-2006GB/T1695-2005GB/T3333HG/T 3330GB12656ASTM D149

    BEST-121体积表面电阻率测定仪(符合国标GB/T 1410243910581169212703.410064ASTM D257-99

    BQYH-96塑料球压痕硬度计(符合国标GB/T3398-2008

    BEST-19导体材料电阻率测试仪

    M-200橡胶塑料滑动摩擦试验机(国标,非国标,可定制)

    GDAT-A介电常数介质损耗测试仪(可测试固体液体

    BQS-37A高频介电常数介质损耗测试仪

    BDH-20KV绝缘材料耐电弧性能试验仪/高电压小电流测试仪

    BWK-300A液显热变形维卡软化点温度测定仪

    BQYH-96塑料球压痕硬度计

    BRT-400Z熔体流动速率测定仪/熔融指数仪

    BMD-A计算机控制马丁耐

    HMYX-2000海绵泡沫压陷硬度测定仪

    HMLQ-500海绵泡沫落球回弹仪

    HMPL-2000海绵泡沫疲劳冲击测定仪

    HMLS-1000海绵拉伸强度试验机

    HMYS-200海绵压缩永久变形试验机

    HMMD-A海绵密度测定仪

    JF-3氧指数测定仪

    XCY-III低温脆性试验机

    BLD-600V漏电起痕试验仪

    BLD-6000V高压漏电起痕试验仪

    BLC-2000落球冲击试验机

    BLB-30管材落镖冲击试验机

    BCM-03摆锤薄膜冲击试验机

    CZF-5水平垂直燃烧试验仪

    BZR-A汽车内饰材料阻燃性能试验机

    BYL-01哑铃制样机

    BJ-50简支梁冲击试验机  

    BX-50悬臂梁冲击试验机

    BM-201门尼粘度试验机

    BL-200无转子硫化仪

    cp-s冲片机手动  

    cp-q气动冲片机

     

    现代科学仪器网安卓版APP

    信息早获取,仪器随时看